Lawrence Livermore develops method to measure residual stress in 3-D printed metal parts

November 17, 2014

LIVERMORE, Calif. - Lawrence Livermore National Laboratory researchers have developed an efficient method to measure residual stress in metal parts produced by powder-bed fusion additive manufacturing.

This 3D printing process produces metal parts layer by layer using a high-energy laser beam to fuse metal powder particles. When each layer is complete, the build platform moves downward by the thickness of one layer, and a new powder layer is spread on the previous layer.

While this process is able to produce quality parts and components, residual stress is a major problem during the fabrication process. That's because large temperature changes near the last melt spot - rapid heating and cooling - and the repetition of this process result in localized expansion and contraction, factors that cause residual stress.

Aside from their potential impact on mechanical performance and structural integrity, residual stresses may cause distortions during processing resulting in a loss of net shape, detachment from support structures and, potentially, the failure of additively manufacturing (AM) parts and components.

An LLNL research team, led by engineer Amanda Wu, has developed an accurate residual stress measurement method that combines traditional stress-relieving methods (destructive analysis) with modern technology: digital image correlation (DIC). This process is able to provide fast and accurate measurements of surface-level residual stresses in AM parts.

The team used DIC to produce a set of quantified residual stress data for AM, exploring laser parameters. DIC is a cost-effective, image analysis method in which a dual camera setup is used to photograph an AM part once before it's removed from the build plate for analysis and once after. The part is imaged, removed and then re-imaged to measure the external residual stress.

In a part with no residual stresses, the two sections should fit together perfectly and no surface distortion will occur. In AM parts, residual stresses cause the parts to distort close to the cut interface. The deformation is measured by digitally comparing images of the parts or components before and after removal. A black and white speckle pattern is applied to the AM parts, so that the images can be fed into a software program that produces digital illustrations of high to low distortion areas on the part's surface.

In order to validate their results from DIC, the team collaborated with Los Alamos National Laboratory (LANL) to perform a residual stress test using a method known as neutron diffraction (ND). This technique, performed by LANL researcher Donald Brown, measures residual stresses deep within a material by detecting the diffraction of an incident neutron beam. The diffracted beam of neutrons enables the detection of changes in atomic lattice spacing due to stress.

Although it's highly accurate, ND is rarely used to measure residual stress because there are only three federal research labs in the U.S. - LANL being one of them - that have the high-energy neutron source required for this analysis.

The LLNL team's DIC results were validated by the ND experiments, showing that DIC is a reliable way to measure residual stress in powder-bed fusion AM parts.

Their findings were the first to provide quantitative data showing internal residual stress distributions in AM parts as a function of laser power and speed. The team demonstrated that reducing the laser scan vector length instead of using a continuous laser scan regulates temperature changes during processing to reduce residual stress. Furthermore, the results show that rotating the laser scan vector relative to the AM part's largest dimension also helps reduce residual stress. The team's results confirm qualitative data from other researchers that reached the same conclusion.

By using DIC, the team was able to produce reliable quantitative data that will enable AM researchers to optimally calibrate process parameters to reduce residual stress during fabrication. Laser settings (power and speed) and scanning parameters (pattern, orientation angle and overlaps) can be adjusted to produce more reliable parts. Furthermore, DIC allowed the Lawrence Livermore team to evaluate the coupled effects of laser power and speed, and to observe a potentially beneficial effect of subsurface layer heating on residual stress development.

"We took time to do a systematic study of residual stresses that allowed us to measure things that were not quantified before," Wu said. "Being able to calibrate our AM parameters for residual stress minimization is critical."

LLNL's findings will eventually be used to help qualify properties of metal parts built using the powder-bed fusion AM process. The team's research helps build on other qualification processes designed at LLNL to improve quality and performance of 3D printed parts and components.
Wu and her colleagues are part of LLNL's Accelerated Certification of Additively Manufactured Metals (ACAMM) Strategic Initiative ( The other members of the Lawrence Livermore team include Wayne King, Gilbert Gallegos and Mukul Kumar.

The team's results were reported in an article titled "An experimental investigation into additive manufacturing-induced residual stresses in 316L stainless steel" that was recently published in the journal Metallurgical and Materials Transactions.

Founded in 1952, Lawrence Livermore National Laboratory provides solutions to our nation's most important national security challenges through innovative science, engineering and technology. Lawrence Livermore National Laboratory is managed by Lawrence Livermore National Security, LLC for the U.S. Department of Energy's National Nuclear Security Administration.

DOE/Lawrence Livermore National Laboratory

Related Stress Articles from Brightsurf:

Stress-free gel
Researchers at The University of Tokyo studied a new mechanism of gelation using colloidal particles.

Early life stress is associated with youth-onset depression for some types of stress but not others
Examining the association between eight different types of early life stress (ELS) and youth-onset depression, a study in JAACAP, published by Elsevier, reports that individuals exposed to ELS were more likely to develop a major depressive disorder (MDD) in childhood or adolescence than individuals who had not been exposed to ELS.

Red light for stress
Researchers from the Institute of Industrial Science at The University of Tokyo have created a biphasic luminescent material that changes color when exposed to mechanical stress.

How do our cells respond to stress?
Molecular biologists reverse-engineer a complex cellular structure that is associated with neurodegenerative diseases such as ALS

How stress remodels the brain
Stress restructures the brain by halting the production of crucial ion channel proteins, according to research in mice recently published in JNeurosci.

Why stress doesn't always cause depression
Rats susceptible to anhedonia, a core symptom of depression, possess more serotonin neurons after being exposed to chronic stress, but the effect can be reversed through amygdala activation, according to new research in JNeurosci.

How plants handle stress
Plants get stressed too. Drought or too much salt disrupt their physiology.

Stress in the powerhouse of the cell
University of Freiburg researchers discover a new principle -- how cells protect themselves from mitochondrial defects.

Measuring stress around cells
Tissues and organs in the human body are shaped through forces generated by cells, that push and pull, to ''sculpt'' biological structures.

Cellular stress at the movies
For the first time, biological imaging experts have used a custom fluorescence microscope and a novel antibody tagging tool to watch living cells undergoing stress.

Read More: Stress News and Stress Current Events is a participant in the Amazon Services LLC Associates Program, an affiliate advertising program designed to provide a means for sites to earn advertising fees by advertising and linking to