Metallic lithium is considered as the ultimate anode material of next-generation high-performance energy storage system, owing to its ultrahigh theoretical specific capacity (3860 mA h g -1 ), ultralow electrochemical potential (-3.04 V vs. the standard hydrogen electrode), and low density (0.534 g cm -3 ). Employing Li metal as high-capacity anode, solid-state lithium-metal batteries (SSLMBs) are becoming one of the most promising candidates for next-generation energy storage devices, due to their high safety and potential high energy density. SSLMBs are expected to be the future for conventional lithium-ion batteries. However, the development of SSLMBs is still limited, due to the severe safety issues caused by the uncontrolled Li dendrite formation and growth. Besides, the strategies focusing on healing or recycling solid electrolytes with Li dendrite penetration are rarely reported.
Recently, a study is led by the group of Prof. Wei Liu (School of Physical Science and Technology, ShanghaiTech University). In this study, they demonstrate a facile method for healing and recycling garnet electrolytes (Ta doped Li 7 La 3 Zr 2 O 12 : LLZTO) with Li dendrites through heat treatment. Excitingly, the recycled garnet ceramic pellets have increased ionic conductivity with higher relative density, which is due to the dendrite-derived species (LiOH and Li 2 CO 3 ) in the grain boundaries are able to promote further densification of garnet electrolyte pellets during thermal healing process as sintering aids (Figure). Compared with pristine garnet electrolyte pellets, the relative density of the recycled garnet pellets is improved from 90.9% to 95.3%, and ionic conductivity is improved from 0.39 to 0.62 mS cm -1 . Benefited from the enhanced relative density and ionic conductivity, a higher critical current density (CCD) is achieved, suggesting a better suppression effect on Li dendrite penetration.
See the article:
Recycling of garnet solid electrolytes with lithium-dendrite penetration by thermal healing
https://link.springer.com/article/10.1007/s40843-022-2371-9
Science China Materials