Iron-aluminum alloys are attractive for high-temperature applications because of their excellent oxidation resistance, relatively low density, and low cost. However, their inherent brittleness at room temperature poses significant challenges for manufacturing. While wire-based arc additive manufacturing offers a flexible fabrication route, repeated thermal cycles during layer-by-layer deposition can alter the grain structure and mechanical properties of the resulting alloy.
In a study published in the KeAi journal China Welding , researchers from Shanghai Jiao Tong University and collaborating institutions examined how deposition current affects the microstructure and mechanical properties of an iron-aluminum alloy. The findings underscore how Fe 3 AlC 0.5 precipitates suppress grain growth and preserve microstructural stability across varying deposition currents, and further elucidate how current settings modulate tensile strength and anisotropy, providing guidance to optimize the TW-DED-arc process for Fe 3 Al-based alloys.
Using twin-wire directed energy deposition-arc (TW-DED-arc), the team fabricated the alloy layer by layer by feeding separate steel and aluminum wires into a common molten pool. During deposition, Fe 3 AlC 0.5 carbide precipitates formed in the alloy.
“These carbide particles play an important role in controlling grain growth during repeated heating,” says corresponding author Chen Shen. “We wanted to understand whether they could help maintain a stable microstructure when the deposition current changes.”
The researchers produced 50-layer deposits at three deposition currents—105, 115, and 125 A—and examined the temperature distribution, microstructure, and mechanical properties of the resulting alloys.
“As deposition current increased, the molten pool reached higher temperatures, and the carbide precipitates grew larger and became more continuously distributed along grain boundaries,” shares Shen. “Despite these changes, the precipitates helped restrict grain growth, keeping the microstructure relatively stable. Average microhardness also varied little across the three conditions.”
Tensile testing, however, revealed a trade-off between strength and anisotropy. “At 115 A, the alloy achieved its highest tensile strengths—approximately 431 MPa in the horizontal direction and 327 MPa in the vertical direction—but also showed the greatest difference between the two directions. Increasing the current to 125 A reduced this difference, although it did not further improve tensile strength,” says Shen.
Notably, the highest strength and the smallest difference between testing directions were achieved at different currents. “This highlights the importance of balancing mechanical properties when selecting deposition parameters,” says Shen.
Contact the author: Chen Shen, Shanghai Key Lab of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, China. Email: cshen486@sjtu.edu.cn
The publisher KeAi was established by Elsevier and China Science Publishing & Media Ltd to unfold quality research globally. In 2013, our focus shifted to open access publishing. We now proudly publish more than 300 world-class, open access, English language journals, spanning all scientific disciplines. Many of these are titles we publish in partnership with prestigious societies and academic institutions, such as the National Natural Science Foundation of China (NSFC).
China Welding
Effect of deposition current on Fe3AlC0.5 precipitation in Fe3Al alloy fabricated via twin-wire directed energy deposition-arc process
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.