Buildings devour roughly 40% of global final energy, and windows are the weakest thermal link. Glass invites glare, summer overheating and winter heat loss; double-glazing helps but raises cost, weight and embodied CO 2 . Now a multidisciplinary team has fabricated a biodegradable window from one of the planet’s fastest-growing plants—bamboo—that behaves almost like living skin, darkening when hot and clearing when cool.
Writing in the Journal of Bioresources and Bioproducts , the authors detail a surprisingly simple route: soak flattened bamboo boards in peroxyacetic acid at 60 °C for six hours to dissolve light-absorbing lignin while sparing load-bearing cellulose and hemicellulose, then compress the delignified mat at 20 MPa and 35°C until its thickness shrinks 80%. The resulting slab is denser (1.33 g cm -3 ) than untreated bamboo yet retains the original nanofibril alignment, yielding record tensile strength of 870 MPa—triple that of natural bamboo and higher than any previously reported transparent biomass material. Three-point bending gives 276 MPa flexural strength and 16.9 GPa modulus, while impact toughness reaches 6.35 J cm -2 , enough to shrug off blows that would shatter glass.
Although lignin removal turns the material white, the tight packing of index-matched cellulose pushes visible-light transmission to 78% with a useful 86% haze that scatters glare and evens indoor illumination. When a 10 µm skin of polylactic acid containing 200 nm W-VO 2 particles is blade-coated onto the surface, the window acquires thermochromic intelligence. At 20°C the coating transmits 42% of visible and 55% of near-infrared light; at 50°C the VO 2 switches to a metallic phase, cutting solar heat gain by 9.7% without compromising daylight.
EnergyPlus modelling of a 5 m × 5 m × 3 m single-zone building fitted with 10 m 2 of the smart bamboo shows annual HVAC savings of 5.58% in Guangzhou’s hot-summer zone, 3.2% in Nanjing’s mixed climate and 1.6% in Beijing, while Harbin’s severe-cold region gains only marginal benefit. Cradle-to-gate life-cycle assessment per cubic metre shows the composite reduces global-warming potential by 35%, particulate-matter formation by 46% and human-toxicity indicators by 40–60% relative to ordinary single glass, and performs even better against Portland cement. End-of-life biodegradation returns W-VO 2 particles for recovery, eliminating landfill waste.
The authors say the process can be scaled with existing bamboo-panel lines and continuous roll-to-roll coating, potentially delivering 2 m × 1 m panes at costs competitive with low-E glass once production exceeds 10,000 m 2 yr -1 . They caution that long-term UV stability and fire performance must still meet building codes, but note that cellulose’s intrinsic char-forming behaviour could offer natural flame retardancy. If adopted widely, they estimate that retrofitting China’s 40 billion m 2 of building façade with such windows could save 150 TWh of electricity annually—roughly the output of the Three Gorges Dam.
See the article:
DOI
https://doi.org/10.1016/j.jobab.2025.11.001
Original Source URL
https://www.sciencedirect.com/science/article/pii/S2369969825000702
Journal
Journal of Bioresources and Bioproducts
Experimental study
Not applicable
Sustainable Transparent Bamboo/W-VO2 Composites for Solar Modulation and Energy-Efficient Buildings
12-Nov-2025